For the part designer, the focus is on the functionality of the molded part, not on the plastic-compatible design, which is precisely what compact injection molding requires. This book describes the necessary fundamentals of physical foam injection molding, clearly illustrated by means of detailed, industrially proven examples to show the technology's potential. Machine and mold technology are also explained in detail, and polymers suitable for the process are discussed. The focus is always on the question of whether the potential of physical foam injection molding has already been exhausted or whether it is emerging as a second standard process alongside compact injection molding.
The experienced authors make it possible to look beyond the end of one's nose. The reader can see which plastic parts can be converted from compact to foam injection molding, and is encouraged to rethink the part design. With this book, specialists are able to examine an application for their own company and analyze it with regard to its economic implementation. However, the book also shows the clear limitations of this technology.
Content:
Foam Injection Molding and its Different Process Variants
Definition and Characteristics of Physical Foam Injection Molding
Design Guidelines for Foamed Components
Polymers for Foam Injection Molding
Process Simulation
Mechanical Fundamentals of the Foam Injection Molding System
Mold Technology
Application Examples: Automotive/Household/Packaging/Medical
Dr. Hartmut Traut holds a degree in industrial management and a doctorate in business administration. After selling his company Centro Kontrollsysteme, he worked for 8 years as Sales and Marketing Director at Thermo Detection, responsible for Europe, Middle East, and Africa. He then served as Trexel's Business Director for Europe for 19 years. In recognition of his many years of service and his role in the development of Trexel, the company has awarded him the honorary title of 'Vice President Emeritus'.
3 | Definition and Characteristics of Physical Foam Injection Molding |
Thermoplastic, foamed molded parts are produced by injection molding by adding a blowing agent to the polymer. A distinction is made between chemical and physical blowing agents. The chemical blowing agents are offered to the processing industry as masterbatch. During the decomposition process of the masterbatch, in addition to the proportion of blowing gas, other residual materials are produced during injection molding that remain in the molded part. Physical blowing agents are mainly the inert gases nitrogen (N2) and carbon dioxide (CO2), which are present in various aggregate states from gaseous to supercritical during processing.
Independent of both the TSG process and the blowing agent used, the molded body is in the form of a structural foam, with a core of closed bubbles, also known as cells, and a compact boundary layer (skin) on both sides.
Foam injection molding brings more than just weight advantages. In addition to the component quality, the design freedom for the component designer increases!
The properties of structural foams are derived from this characteristic structure, and thus ultimately also determine the material parameters for the component designer. By varying the boundary layer thickness as well as the cell size, cell density and cell orientation (in the case of elliptical cells), the property can also be partially optimized in line with the load. If one considers the two phases of the production of a single-phase mixture of matrix polymer and blowing gas in the injection molding machine, and the production of the molded part in the cavity of the mold, it is clear that not only the process parameters of the injection molding machine are critical, but that the mold also makes a significant contribution to the structural properties. Last but not least, in addition to the polymer to be processed, the proportion or type of nucleating agent also plays a role. At first glance, this apparent complexity in foam production appears difficult, but in the end, for the expert who masters his/her profession, there are possible solutions in lightweight design that cannot be achieved in any other comparable cost-effective way. Let us therefore go into the details.
3.1 | Properties of TSG Structural Foams |
Figure 3.1 Example of a structural foam [Source: NMB GmbH, Bayreuth, Germany]
In Figure 3.1, we see a typical example of a structural foam. Such a structure appears independent of the blowing agent used and independent of the manufacturing technology. A compact boundary layer and a foamed core can be seen, with the density usually increasing slightly from the center axis of the core to the boundary layer. The mechanical properties of such a structure – also called integral foam – which are important for the component designer can be used to advantage in component design.
However, until we go into this in more detail later, a quote from Cramer’s dissertation from 2008 [1] should explain the status at that time:
“Another challenge is found in the mechanical properties of thermoplastic foams. Basically, their mechanics are reduced by the absence of load-transmitting material compared to compact components with the same dimensions. This applies to components loaded in tension, in bending, as well as in impact. Only if the properties are normalized to the weight can better mechanical properties be achieved, depending on the load case. The sandwich-like structure of injection-molded thermoplastic foams results in a high area moment of inertia at low weight, which can mainly improve the load absorption in relation to weight under bending stress compared to compact injection molding. However, this potential often remains unused because in many cases the molded parts are designed according to conventional injection molding criteria. One reason is the often-cited lack of knowledge of the relationships between the foam structures and the resulting mechanical properties. A prediction of the molding process, let alone a structural simulation of the manufactured parts, is not yet possible today, despite many years of work in this field. However, this prediction must be a long-term goal in order to enable and expand the use of foamed components as technical injection molded articles.”
This quotation reflects the correct state of the art at that time! However, all the unsolved problems mentioned at that time will be taken up and answered in this book, especially in Chapters 4 (Design Guidelines) and 5 (Simulation). So there are effectively no more open questions today!
Ask your component designer if he or she knows the difference between plastic-compliant design in compact injection molding and foam injection molding? If not, change designers or train your designer for both use cases.
3.1.1 | Weight Reduction |
Typical weight reductions of finished parts are between 5% and 15%, depending on the material used (polymer and amount of blowing agent) and the process conditions during the production of the molded part. However, since the material parameters required for the design of the part depend on the thickness of the surface layer and the cell structure, any desired high weight reduction always competes with the necessary and sufficient material properties. For design reasons, this always leads to compromises.
3.1.2 | Sink Marks |
Sink marks can be almost completely eliminated on the molded parts – especially in the case of wall thickness variations – because the necessary pressure in the mold has an almost uniform effect on the polymer melt from the inside due to the blowing agent. This provides the part designer with a great deal of additional potential: In contrast to the familiar plastic-specific design, in which there is a considerable pressure difference between the sprue and the end of the flow line inside the cavity in the holding pressure phase, the mechanical requirements of rib structures, for example, can be made more suitable for lightweight design with a view to notch effects or force transmission. See also Figure 3.2 for an explanation.
Figure 3.2 Avoidance of sink marks with TSG [Source: Engel Austria GmbH, Austria]
3.1.3 | Part Warpage |
The process also dramatically reduces the warpage of the molded parts. As already mentioned in the previous chapter, the pressure required to form the single-phase mixture in the cavity is generated “from within” by the blowing gas. No holding pressure is required. The residual stresses and frozen orientations of the molecular chains typical of injection molding are minimized. As a result, components can then be manufactured with much tighter tolerances for the subsequent assembly process with a better fit.
Figure 3.3 Test results with greatly reduced warpage [Source: Trexel GmbH, Germany]
3.1.4 | Shrinkage Behavior |
In general, TSG foams are produced with lower shrinkage behavior than the classic injection molded parts. However, this must be divided into different shrinkage behavior in the thickness and longitudinal directions [2]. The observed shrinkage in the thickness direction is significantly lower than in compact injection molding, whereas a look at longitudinal shrinkage shows little to no difference from the known shrinkage behavior of classic injection molding.
This different behavior can be well understood based on the integral foam shown in Figure 3.1: In the thickness direction, the bubble growth inside the integral foam directly counteracts shrinkage. In the longitudinal direction, on the other hand, the compact boundary layers of the structural foam act similarly to a compact component, while the bubble growth has no major influence. This means that the shrinkage behavior is also similar.
3.1.5 | Mechanical Properties |
The mechanical properties of structural foams can be varied within a certain range by the process conditions. For the bending stress or the bending modulus, the main influence is the boundary layer thickness. The main influence on stresses and elongations at break, on the other hand, is determined by the density of the component [3], as Figure 3.4 shows well. More detailed information on this and the different influences on amorphous or semi-crystalline thermoplastic materials can be found in Chapter 6 “Polymers for Foam Injection Molding”.
Figure 3.4 Flexural stress in a component made of PBT. The chart shows the main influence of the boundary layer thickness on the flexural modulus, whereas the component density exerts the main influence on stresses and elongations at break [Source: IKV Aachen, Germany [3], Copyright: Kunststoffe, Hanser Verlag, Germany]
3.1.6 | Insulation Behavior against Temperature Gradients |
It is well known that foams insulate against heat/cold, which of course also applies to structural foams. In particular, the cell size, but also the cell uniformity, plays the main role. The heat transfer decreases,...
Erscheint lt. Verlag | 6.5.2024 |
---|---|
Zusatzinfo | in full colour |
Sprache | englisch |
Themenwelt | Naturwissenschaften ► Chemie |
Technik | |
Schlagworte | blowing agents • foaming • lightweight plastic • Manufacturing • physical foaming • Plastic part design • Plastics • Plastics Engineering • plastics technology |
ISBN-10 | 1-56990-383-2 / 1569903832 |
ISBN-13 | 978-1-56990-383-4 / 9781569903834 |
Haben Sie eine Frage zum Produkt? |
![PDF](/img/icon_pdf_big.jpg)
Größe: 17,7 MB
DRM: Digitales Wasserzeichen
Dieses eBook enthält ein digitales Wasserzeichen und ist damit für Sie personalisiert. Bei einer missbräuchlichen Weitergabe des eBooks an Dritte ist eine Rückverfolgung an die Quelle möglich.
Dateiformat: PDF (Portable Document Format)
Mit einem festen Seitenlayout eignet sich die PDF besonders für Fachbücher mit Spalten, Tabellen und Abbildungen. Eine PDF kann auf fast allen Geräten angezeigt werden, ist aber für kleine Displays (Smartphone, eReader) nur eingeschränkt geeignet.
Systemvoraussetzungen:
PC/Mac: Mit einem PC oder Mac können Sie dieses eBook lesen. Sie benötigen dafür einen PDF-Viewer - z.B. den Adobe Reader oder Adobe Digital Editions.
eReader: Dieses eBook kann mit (fast) allen eBook-Readern gelesen werden. Mit dem amazon-Kindle ist es aber nicht kompatibel.
Smartphone/Tablet: Egal ob Apple oder Android, dieses eBook können Sie lesen. Sie benötigen dafür einen PDF-Viewer - z.B. die kostenlose Adobe Digital Editions-App.
Buying eBooks from abroad
For tax law reasons we can sell eBooks just within Germany and Switzerland. Regrettably we cannot fulfill eBook-orders from other countries.
![EPUB](/img/icon_epub_big.jpg)
Größe: 23,8 MB
DRM: Digitales Wasserzeichen
Dieses eBook enthält ein digitales Wasserzeichen und ist damit für Sie personalisiert. Bei einer missbräuchlichen Weitergabe des eBooks an Dritte ist eine Rückverfolgung an die Quelle möglich.
Dateiformat: EPUB (Electronic Publication)
EPUB ist ein offener Standard für eBooks und eignet sich besonders zur Darstellung von Belletristik und Sachbüchern. Der Fließtext wird dynamisch an die Display- und Schriftgröße angepasst. Auch für mobile Lesegeräte ist EPUB daher gut geeignet.
Systemvoraussetzungen:
PC/Mac: Mit einem PC oder Mac können Sie dieses eBook lesen. Sie benötigen dafür die kostenlose Software Adobe Digital Editions.
eReader: Dieses eBook kann mit (fast) allen eBook-Readern gelesen werden. Mit dem amazon-Kindle ist es aber nicht kompatibel.
Smartphone/Tablet: Egal ob Apple oder Android, dieses eBook können Sie lesen. Sie benötigen dafür eine kostenlose App.
Geräteliste und zusätzliche Hinweise
Buying eBooks from abroad
For tax law reasons we can sell eBooks just within Germany and Switzerland. Regrettably we cannot fulfill eBook-orders from other countries.
aus dem Bereich